Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Organic–inorganic covalent–ionic molecules for elastic ceramic plastic

Abstract

Although organic–inorganic hybrid materials have played indispensable roles as mechanical1,2,3,4, optical5,6, electronic7,8 and biomedical materials9,10,11, isolated organic–inorganic hybrid molecules (at present limited to covalent compounds12,13) are seldom used to prepare hybrid materials, owing to the distinct behaviours of organic covalent bonds14 and inorganic ionic bonds15 in molecular construction. Here we integrate typical covalent and ionic bonds within one molecule to create an organic–inorganic hybrid molecule, which can be used for bottom-up syntheses of hybrid materials. A combination of the organic covalent thioctic acid (TA) and the inorganic ionic calcium carbonate oligomer (CCO) through an acid–base reaction provides a TA–CCO hybrid molecule with the representative molecular formula TA2Ca(CaCO3)2. Its dual reactivity involving copolymerization of the organic TA segment and inorganic CCO segment generates the respective covalent and ionic networks. The two networks are interconnected through TA–CCO complexes to form a covalent–ionic bicontinuous structure within the resulting hybrid material, poly(TA–CCO), which unifies paradoxical mechanical properties. The reversible binding of Ca2+–CO32− bonds in the ionic network and S–S bonds in the covalent network ensures material reprocessability with plastic-like mouldability while preserving thermal stability. The coexistence of ceramic-like, rubber-like and plastic-like behaviours within poly(TA–CCO) goes beyond current classifications of materials to generate an ‘elastic ceramic plastic’. The bottom-up creation of organic–inorganic hybrid molecules provides a feasible pathway for the molecular engineering of hybrid materials, thereby supplementing the classical methodology used for the manufacture of organic–inorganic hybrid materials.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: TA–CCO hybrid molecules.
Fig. 2: Covalent–ionic bicontinuous network.
Fig. 3: Mechanical properties of the poly(TA–CCO) bulk.
Fig. 4: Structural reversibility of reprocessable poly(TA–CCO) bulk.

Similar content being viewed by others

Data availability

All the relevant data are available from the corresponding authors on reasonable request. Source data are provided with this paper.

References

  1. Kinloch, I. A., Suhr, J., Lou, J., Young, R. J. & Ajayan, P. M. Composites with carbon nanotubes and graphene: an outlook. Science 362, 547–553 (2018).

    Article  CAS  PubMed  ADS  Google Scholar 

  2. Zou, H., Wu, S. & Shen, J. Polymer/silica nanocomposites: preparation, characterization, properties, and applications. Chem. Rev. 108, 3893–3957 (2008).

    Article  CAS  PubMed  Google Scholar 

  3. Picker, A. et al. Mesocrystalline calcium silicate hydrate: a bioinspired route toward elastic concrete materials. Sci. Adv. 3, e1701216 (2017).

    Article  PubMed  PubMed Central  Google Scholar 

  4. Li, C. et al. Fiber-based biopolymer processing as a route toward sustainability. Adv. Mater. 34, e2105196 (2022).

    Article  PubMed  Google Scholar 

  5. Pansare, A. V. et al. In situ nanoparticle embedding for authentication of epoxy composites. Adv. Mater. 30, e1801523 (2018).

    Article  Google Scholar 

  6. Xu, W. J. et al. Molecular dynamics of flexible polar cations in a variable confined space: toward exceptional two-step nonlinear optical switches. Adv. Mater. 28, 5886–5890 (2016).

    Article  CAS  PubMed  Google Scholar 

  7. Huang, X., Qi, X., Boey, F. & Zhang, H. Graphene-based composites. Chem. Soc. Rev. 41, 666–686 (2012).

    Article  CAS  PubMed  Google Scholar 

  8. Vijayakanth, T., Liptrot, D. J., Gazit, E., Boomishanka, R. & Bowen, C. R. Recent advances in organic and organic–inorganic hybrid materials for piezoelectric mechanical energy harvesting. Adv. Funct. Mater. 32, 2109492 (2022).

    Article  CAS  Google Scholar 

  9. Park, W. et al. Advanced hybrid nanomaterials for biomedical applications. Prog. Mater. Sci. 114, 100686 (2020).

    Article  CAS  Google Scholar 

  10. Kim, Y. C. et al. Printable organometallic perovskite enables large-area, low-dose X-ray imaging. Nature 550, 87–91 (2017).

    Article  CAS  PubMed  ADS  Google Scholar 

  11. Kumar, S. et al. Recent advances and remaining challenges for polymeric nanocomposites in healthcare applications. Prog. Polym. Sci. 80, 1–38 (2018).

    Article  CAS  Google Scholar 

  12. Sanchez, C., Belleville, P., Popall, M. & Nicole, L. Applications of advanced hybrid organic–inorganic nanomaterials: from laboratory to market. Chem. Soc. Rev. 40, 696–753 (2011).

    Article  CAS  PubMed  Google Scholar 

  13. Spange, S. & Grund, S. Nanostructured organic–inorganic composite materials by twin polymerization of hybrid monomers. Adv. Mater. 21, 2111–2116 (2009).

    Article  CAS  Google Scholar 

  14. Lewis, G. N. The atom and the molecule. J. Am. Chem. Soc. 38, 762–785 (2002).

    Article  Google Scholar 

  15. Kossel, W. Über molekülbildung als frage des atombaus. Ann. Phys. 354, 229–362 (1916).

    Article  Google Scholar 

  16. Sanchez, C., Shea, K. J. & Kitagawa, S. Recent progress in hybrid materials science. Chem. Soc. Rev. 40, 471–472 (2011).

    Article  CAS  PubMed  Google Scholar 

  17. Thanh, N. T., Maclean, N. & Mahiddine, S. Mechanisms of nucleation and growth of nanoparticles in solution. Chem. Rev. 114, 7610–7630 (2014).

    Article  CAS  PubMed  Google Scholar 

  18. De Yoreo, J. J. & Vekilov, P. G. Principles of crystal nucleation and growth. Rev. Mineral. Geochem. 54, 57–93 (2003).

    Article  Google Scholar 

  19. Nielsen, M. H., Aloni, S. & De Yoreo, J. J. In situ TEM imaging of CaCO3 nucleation reveals coexistence of direct and indirect pathways. Science 345, 1158–1162 (2014).

    Article  CAS  PubMed  ADS  Google Scholar 

  20. Markovic, G. & Visakh, P. M. Recent Developments in Polymer Macro, Micro and Nano Blends (Woodhead Publishing, 2017).

  21. Laine, R. M., Choi, J. & Lee, I. Organic–inorganic nanocomposites with completely defined interfacial interactions. Adv. Mater. 13, 800–803 (2001).

    Article  CAS  Google Scholar 

  22. Sun, S. T., Mao, L. B., Lei, Z. Y., Yu, S. H. & Cölfen, H. Hydrogels from amorphous calcium carbonate and polyacrylic acid: bio-inspired materials for “mineral plastics”. Angew. Chem. Int. Ed. 55, 11765–11769 (2016).

    Article  CAS  Google Scholar 

  23. Liu, Z. et al. Crosslinking ionic oligomers as conformable precursors to calcium carbonate. Nature 574, 394–398 (2019).

    Article  CAS  PubMed  ADS  Google Scholar 

  24. Thomas, R. C. & Reed, L. J. Disulfide polymers of DL-α-lipoic acid. J. Am. Chem. Soc. 78, 6148–6149 (2002).

    Article  Google Scholar 

  25. Michel, F. M. et al. Structural characteristics of synthetic amorphous calcium carbonate. Chem. Mater. 20, 4720–4728 (2008).

    Article  CAS  Google Scholar 

  26. Dang, C. et al. Transparent, highly stretchable, rehealable, sensing, and fully recyclable ionic conductors fabricated by one‐step polymerization based on a small biological molecule. Adv. Funct. Mater. 29, 1902467 (2019).

    Article  Google Scholar 

  27. Zhang, Q. et al. Exploring a naturally tailored small molecule for stretchable, self-healing, and adhesive supramolecular polymers. Sci. Adv. 4, eaat8192 (2018).

    Article  CAS  PubMed  PubMed Central  ADS  Google Scholar 

  28. Calvo-Correas, T. et al. Advanced and traditional processing of thermoplastic polyurethane waste. Polym. Degrad. Stab. 198, 109880 (2022).

    Article  CAS  Google Scholar 

  29. Inazu, M. et al. Dynamic hetero-metallic bondings visualized by sequential atom imaging. Nat. Commun. 13, 2968 (2022).

    Article  CAS  PubMed  PubMed Central  ADS  Google Scholar 

  30. Teubner, M. & Strey, R. Origin of the scattering peak in microemulsions. J. Chem. Phys. 87, 3195–3200 (1987).

    Article  CAS  ADS  Google Scholar 

  31. Mihailescu, M. et al. Dynamics of bicontinuous microemulsion phases with and without amphiphilic block-copolymers. J. Chem. Phys. 115, 9563–9577 (2001).

    Article  CAS  ADS  Google Scholar 

  32. Bates, F. S. et al. Polymeric bicontinuous microemulsions. Phys. Rev. Lett. 79, 849–852 (1997).

    Article  CAS  ADS  Google Scholar 

  33. Seo, M. & Hillmyer, M. A. Reticulated nanoporous polymers by controlled polymerization-induced microphase separation. Science 336, 1422–1425 (2012).

    Article  CAS  PubMed  ADS  Google Scholar 

  34. Yamamoto, K., Ito, E., Fukaya, S. & Takagi, H. Phase-separated conetwork structure induced by radical copolymerization of poly(dimethylsiloxane)-α,ω-diacrylate and N,N-dimethylacrylamide. Macromolecules 42, 9561–9567 (2009).

    Article  CAS  ADS  Google Scholar 

  35. Zok, F. W. & Miserez, A. Property maps for abrasion resistance of materials. Acta Mater. 55, 6365–6371 (2007).

    Article  CAS  PubMed  PubMed Central  ADS  Google Scholar 

  36. Field, J. S., Swain, M. V. & Dukino, R. D. Determination of fracture toughness from the extra penetration produced by indentation-induced pop-in. J. Mater. Res. 18, 1412–1419 (2011).

    Article  ADS  Google Scholar 

  37. Musil, J. Flexible hard nanocomposite coatings. RSC Adv. 5, 60482–60495 (2015).

    Article  CAS  ADS  Google Scholar 

  38. CES Edupack 2023 (Granta Design, 2023).

  39. Li, J. et al. Deformation behavior of nanoporous gold based composite in compression: a finite element analysis. Compos. Struct. 211, 229–235 (2019).

    Article  Google Scholar 

  40. Griffiths, E., Wilmers, J., Bargmann, S. & Reddy, B. D. Nanoporous metal based composites: giving polymers strength and making metals move. J. Mech. Phys. Solids 137, 103848 (2020).

    Article  MathSciNet  CAS  Google Scholar 

  41. Madhukar, M. S. & Drzal, L. T. Fiber-matrix adhesion and its effect on composite mechanical properties: I. Inplane and interlaminar shear behavior of graphite/epoxy composites. J. Compos. Mater. 25, 932–957 (2016).

    Article  Google Scholar 

  42. Li, T. Q., Zhang, M. Q., Zhang, K. & Zeng, H. M. The dependence of the fracture toughness of thermoplastic composite laminates on interfacial interaction. Compos. Sci. Technol. 60, 465–476 (2000).

    Article  CAS  Google Scholar 

  43. Chen, Q., Chasiotis, I., Chen, C. & Roy, A. Nanoscale and effective mechanical behavior and fracture of silica nanocomposites. Compos. Sci. Technol. 68, 3137–3144 (2008).

    Article  CAS  Google Scholar 

  44. Zhang, X. & Waymouth, R. M. 1,2-dithiolane-derived dynamic, covalent materials: cooperative self-assembly and reversible cross-linking. J. Am. Chem. Soc. 139, 3822–3833 (2017).

    Article  CAS  PubMed  Google Scholar 

  45. Mu, Z. et al. Pressure-driven fusion of amorphous particles into integrated monoliths. Science 372, 1466–1470 (2021).

    Article  CAS  ADS  Google Scholar 

  46. Sun, J. Y. et al. Highly stretchable and tough hydrogels. Nature 489, 133–136 (2012).

    Article  CAS  PubMed  PubMed Central  ADS  Google Scholar 

  47. Biellmann, C. & Gillet, P. High-pressure and high-temperature behaviour of calcite, aragonite and dolomite: a Raman spectroscopic study. Eur. J. Mineral. 4, 389–394 (1992).

    Article  CAS  ADS  Google Scholar 

  48. Huang, S. et al. Covalent adaptable liquid crystal networks enabled by reversible ring-opening cascades of cyclic disulfides. J. Am. Chem. Soc. 143, 12543–12551 (2021).

    Article  CAS  PubMed  Google Scholar 

  49. Steudel, R., Passlack-Stephan, S. & Holdt, G. Thermal polymerization and depolymerization reactions of 10 sulfur allotropes studied by HPLC and DSC. Z. Anorg. Allg. Chem. 517, 7–42 (1984).

    Article  CAS  Google Scholar 

  50. Schyns, Z. O. G. & Shaver, M. P. Mechanical recycling of packaging plastics: a review. Macromol. Rapid Commun. 42, e2000415 (2021).

    Article  PubMed  Google Scholar 

  51. Kojima, Y., Kawanobe, A., Yasue, T. & Arai, Y. Synthesis of amorphous calcium carbonate and its crystallization. J. Ceram. Soc. Jpn. 101, 1145–1152 (1993).

    Article  CAS  Google Scholar 

  52. Faatz, M., Gröhn, F. & Wegner, G. Amorphous calcium carbonate: synthesis and potential intermediate in biomineralization. Adv. Mater. 16, 996–1000 (2004).

    Article  CAS  Google Scholar 

  53. Koga, N., Nakagoe, Y. & Tanaka, H. Crystallization of amorphous calcium carbonate. Thermochim. Acta 318, 239–244 (1998).

    Article  CAS  Google Scholar 

  54. Oshida, K. et al. Analysis of pore structure of activated carbon fibers using high resolution transmission electron microscopy and image processing. J. Mater. Res. 10, 2507–2517 (2011).

    Article  ADS  Google Scholar 

  55. Mastronarde, D. N. & Held, S. R. Automated tilt series alignment and tomographic reconstruction in IMOD. J. Struct. Biol. 197, 102–113 (2017).

    Article  PubMed  Google Scholar 

  56. Pettersen, E. F. et al. UCSF Chimera—a visualization system for exploratory research and analysis. J. Comput. Chem. 25, 1605–1612 (2004).

    Article  CAS  PubMed  Google Scholar 

  57. Juhás, P., Davis, T., Farrow, C. L. & Billinge, S. J. L. PDFgetX3: a rapid and highly automatable program for processing powder diffraction data into total scattering pair distribution functions. J. Appl. Crystallogr. 46, 560–566 (2013).

    Article  Google Scholar 

  58. Xi, Y., Lankone, R. S., Sung, L. P. & Liu, Y. Tunable thermo-reversible bicontinuous nanoparticle gel driven by the binary solvent segregation. Nat. Commun. 12, 910 (2021).

    Article  CAS  PubMed  PubMed Central  ADS  Google Scholar 

  59. Schubert, K. V., Strey, R., Kline, S. R. & Kaler, E. W. Small angle neutron scattering near Lifshitz lines: transition from weakly structured mixtures to microemulsions. J. Chem. Phys. 101, 5343–5355 (1994).

    Article  CAS  ADS  Google Scholar 

  60. Oliver, W. C. & Pharr, G. M. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 7, 1564–1583 (2011).

    Article  ADS  Google Scholar 

  61. Pryor, R. W. Multiphysics Modeling Using COMSOL: A First Principles Approach (Jones and Bartlett, 2009).

  62. Lu, T. & Chen, F. Multiwfn: a multifunctional wavefunction analyzer. J. Comput. Chem. 33, 580–592 (2012).

    Article  PubMed  Google Scholar 

  63. Choi, C. et al. Light-mediated synthesis and reprocessing of dynamic bottlebrush elastomers under ambient conditions. J. Am. Chem. Soc. 143, 9866–9871 (2021).

    Article  CAS  PubMed  Google Scholar 

  64. Liu, Y., Jia, Y., Wu, Q. & Moore, J. S. Architecture-controlled ring-opening polymerization for dynamic covalent poly(disulfide)s. J. Am. Chem. Soc. 141, 17075–17080 (2019).

    Article  CAS  PubMed  Google Scholar 

  65. Cai, C., Wu, S., Tan, Z., Li, F. & Dong, S. On-site supramolecular adhesion to wet and soft surfaces via solvent exchange. ACS Appl. Mater. Interfaces 13, 53083–53090 (2021).

    Article  CAS  Google Scholar 

Download references

Acknowledgements

We thank S. Chang and J. Guo for assistance with 3D cryo-TEM tomography reconstruction and FIB-SEM in the Center of Cryo-Electron Microscopy (CCEM), Zhejiang University. We thank the Chemistry Instrumentation Center, Zhejiang University for characterization support, including Y. Qiu for help with SAXS and GPC data analysis; F. Chen for assistance with electron microscopy; Y. Liu for assistance with NMR; Q. He for help with MS; G. Lan for GC-MS analysis; and D. Shi and X. Hu for in situ heating XRD analysis. We thank L. Xu for assistance with DSC and DMA at the State Key Laboratory of Chemical Engineering, Zhejiang University. We thank Y. Li at the University of California, Santa Barbara, for discussions. We thank Ansys for providing software support and Shanghai AIYU Information Technology Co., Ltd for the service support. We acknowledge funding support from the National Natural Science Foundation of China (22022511, 22275161), the National Key Research and Development Program of China (2020YFA0710400) and the Fundamental Research Funds for the Central Universities (226-2022-00022, 2021FZZX001-04).

Author information

Authors and Affiliations

Authors

Contributions

R.T. and Z.L. initiated this project. W.F. synthesized all samples and performed most examinations. Z.M. helped perform HRTEM and analysed the results. W.F. and Y.H. finished the cryo-TEM. K.K. helped perform MS. W.F., Z.M. and K.J. acquired the in situ temperature–pressure Raman data. R.T. and Z.L. supervised and supported the project. W.F., R.T. and Z.L. wrote the manuscript. All authors reviewed and approved the manuscript.

Corresponding authors

Correspondence to Ruikang Tang or Zhaoming Liu.

Ethics declarations

Competing interests

The authors declare no competing interests.

Peer review

Peer review information

Nature thanks Jesus Maria Garcia Martinez and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Fig. 1 Characterization of CCO and TA.

a, Snapshot of the CCO ethanol solution. b, Size distribution of CCO analysed by dynamic light scattering. The mean size of the CCO was 1.25 nm, which corresponded to a typical molecular formula (CaCO3)3 for CCO (ref. 23). c, Snapshot of the TA ethanol solution. d, Mass spectrum of the TA ethanol solution. The main peaks were at m/z = 171 and 205, which were for the characteristic fragment ions of TA.

Source data

Extended Data Fig. 2 Characterization of TA-CCO hybrid molecules.

a, Mass fraction of S and Ca elements in a TA-CCO hybrid molecule, which were measured by ICP-OES, giving an approximate Ca:TA molar ratio of 1.5. Error bars represent standard deviation, n = 8. b,c, Liquid-state 13C NMR spectra of CCO and TA in ethanol. The peaks at 160 ppm and 176 ppm contributed to the carbonate (in CCO) and carboxyl (in TA) groups, respectively. d, The peaks for carbonate and the carboxyl group in TA-CCO have almost similar symmetry to those of pure TA and CCO. The small shoulder (at 181.15 ppm) on the carboxyl group peak was attributed to by-products generated during the reaction. e, TEM image of amorphous CaCO3 nanoparticles (NP) with an average diameter of 41.3 nm. f, Snapshot of a TA-NP mixed ethanol solution. g,h, Liquid-state 13C NMR and mass spectra of the TA-NP mixed solution. The absence of a chemical shift for carbonate indicated the unsuccessful construction of hybrid molecules from CaCO3 nanoparticles.

Source data

Extended Data Fig. 3 Structures of the TA-CCO hybrid molecule and its polymerization.

a, HRTEM images of partial single TA-CCO hybrid molecules with lengths of approximately 3.2 nm. The variation in image contrast implied the coexistence of CaCO3 (higher electron density) and TA (lower electron density) in the TA-CCO hybrid molecule. b, Size of a TA-CCO hybrid molecule calculated with the Multiwfn program62, which was consistent with the HRTEM results. c, Typical chemical shift of tertiary carbon on the carbon ring before and after polymerization indicates ring-opening polymerization of disulfide bonds63,64.

Source data

Extended Data Fig. 4 Optical characterization of poly(TA-CCO) bulk.

a, UV–Vis spectra of poly(TA-CCO) and pTA-NP bulk with the same thicknesses of 2 mm. The poly(TA-CCO) bulk exhibited an average transmittance of 85% at 420–800 nm, whereas it was nontransparent at 200–420 nm. This was because the homogeneous structure of poly(TA-CCO) did not reflect or scatter light. Moreover, the TA absorbed light between wavelengths of 200 and 420 nm. By contrast, the pTA-NP bulk was completely opaque. The heterogeneous structure of pTA-NP caused by the aggregation of nanoparticles scattered all the light, leading to nontransparency. This further confirmed the homogeneity of the poly(TA-CCO) bulk from the microscale to the macroscale, which differs from that of traditional nanocomposites. The inset shows snapshots of poly(TA-CCO) bulk with different shapes, demonstrating the mouldable construction of poly(TA-CCO). b, The enlarged spectra of a over the range 200–400 nm, exhibiting full absorption (over 99.9%) by the poly(TA-CCO) bulk in the ultraviolet region owing to the characteristic ultraviolet absorptions of the organic segments in the TA-CCO hybrid molecule. The inset images demonstrate that fluorescence of the letters under ultraviolet irradiation was prohibited by covering the transparent poly(TA-CCO) bulk over the letters. This suggested that the optical features of the organic segments were preserved in the organic–inorganic hybrid molecule. c, Snapshots of pTA showing the high viscosity, which was commonly used as an adhesive material65. d, SEM image of pTA with a homogeneous structure. e, Snapshots of pTA-NP. f, SEM image of pTA-NP with apparent phase separation of the inorganic and organic phases. The yellow circles represent aggregated CaCO3 nanoparticles.

Source data

Extended Data Fig. 5 Thermal behaviour of poly(TA-CCO).

a, TG-DSC curve of poly(TA-CCO) from room temperature to 1,400 °C. b More detail in a temperature range from 160 to 400 °C. c, In situ XRD patterns of poly(TA-CCO) during the heating and cooling process. The temperature of the heating and cooling cycle began at 25 °C, increased gradually to 70, 100, 130, 160 and 190 °C and finally decreased to 25 °C by the same temperature steps. The results indicated an amorphous feature of poly(TA-CCO) throughout the thermal treatment. d, XRD spectra of the residual composition at different temperatures in the TG-DSC curve. The green circles, pink triangles and red diamonds represent CaSO4, CaCO3 and CaO, respectively. The exact composition of poly(TA-CCO) could be calculated from the TG-DSC and XRD analysis, which indicated a 1.5:1 molar ratio of Ca to TA, which is consistent with the TA-CCO hybrid molecule. e, TG-DSC curve of pTA-NP. The inorganic content was 42 wt%, corresponding to a 1.5:1 molar ratio of Ca to TA that is similar to that of poly(TA-CCO).

Source data

Extended Data Fig. 6 Size statistics for the inorganic and organic bicontinuous networks in poly(TA-CCO).

a, Statistical widths of the inorganic and organic networks. The inset illustration represents a specific 2D projection acquired from the 3D bulk. Owing to tortuous linear-like distributions of inorganic and organic networks, the widths of the networks changed with the position of the slice and direction of the measurement. In a 2D image acquired with FIB and HAADF-STEM, we statistically measured the widths of inorganic and organic networks in a specific direction. The measured widths of the TA and CaCO3 networks varied from 2.2 nm to 3.9 nm and from 1.1 nm to 1.8 nm, respectively. However, the minimum width was fixed, which corresponded to the periodic width of the TA and CaCO3 networks in the 3D structure. b, Molecular weight distribution curve and characteristic molecular weights of residual organic poly(TA) network after dissolving the inorganic network. The molecular weight of the residual poly(TA) was 5.26 × 105 g mol−1 (Mw). Mn is the number average molecular weight, Mw is the weight average molecular weight, Mz is the Z-average molecular weight, Mz+1 is the Z+1 average molecular weight and PDI is the polydispersity index.

Source data

Extended Data Fig. 7 Mechanics of poly(TA-CCO) bulk.

a, Hardness and modulus of pTA, pTA-NP and poly(TA-CCO) bulk. Error bars represent standard deviation, n ≥ 5. b, Snapshots captured from a video of in situ nanoindentation corresponding to the maximum depth and residual impression remaining after unloading the flat indenter. The silicone rubber and poly(TA-CCO) exhibited similar deformation behaviour during loading and unloading. c, AFM height topology of residual Berkovich indentation for a maximum load of 50 mN on poly(TA-CCO). The cross-sectional profiles correspond to the two designated directions indicated by the red and blue lines. The maximum residual depth was 138 nm after 1,813-nm deformation, indicating elastic recovery of the indented surface. d, Variation in the damping factor with increasing temperature for poly(TA-CCO), widely used commodity plastics (PP, PP+CF, ABS, ABS+CF) and engineering plastics (POM and POM+CF). The damping factor for poly(TA-CCO) remained constant before 80 °C and after 160 °C and then slightly increased between 80 and 160 °C, which was close to the temperature of the endothermic peak in DSC. This was because of the breaking of S–S bonds in the organic TA network, which slightly increased the viscosity of poly(TA-CCO). By contrast, the damping factor increased sharply for plastics after the temperature reached their softening temperatures, suggesting a vigorous movement of polymer chains and an increase in viscosity.

Source data

Extended Data Fig. 8 Materials chosen for mechanical comparison in Fig. 3.

The detailed data can be found in Supplementary Tables 2 and 3 in the Supplementary Information. The error bars for each point are not shown to make the figures easy to distinguish.

Extended Data Fig. 9 Finite element simulation of the mechanical response under uniaxial compression.

ac, Finite element model of the covalent–ionic bicontinuous network in poly(TA-CCO). The orange part represents the covalent (TA) network and the blue part represents the ionic (CaCO3) network. b,c, Calculated von Mises stress distributions of the covalent network (b) and the ionic network (c) at strains of 2%, 5% and 10%. This demonstrated the flexibility of the inorganic ionic network without accumulation of stresses. The average stress was 196 MPa for poly(TA-CCO) at a strain of 10%. df, Finite element model of the nanocomposite structure in pTA-NP. The orange part represents the TA matrix and the blue part represents CaCO3 nanoparticles. e,f, Calculated von Mises stress distributions of the TA matrix (e) and CaCO3 nanoparticles (f) at strains of 2%, 5% and 10%. This showed accumulated stress at the organic–inorganic interface, at which the failure of organic–inorganic nanocomposites commonly occurs. The average value of the stress was 22 MPa for pTA-NP.

Extended Data Fig. 10 Internal structure of poly(TA-CCO) bulk after reprocessing.

a, HAADF-STEM image of the reprocessed poly(TA-CCO) bulk showing preservation of the covalent–ionic bicontinuous network. b, Pair distribution functions (denoted by G(r)) of the original poly(TA-CCO) bulk and reprocessed poly(TA-CCO) bulk. No obvious change was observed after reprocessing, which indicated the dynamic structural reversibility of the covalent–ionic bicontinuous network in poly(TA-CCO).

Source data

Supplementary information

Supplementary Information

This file contains Supplementary Notes 1–5, Supplementary Figs. 1–4 and Supplementary Tables 1–3.

Supplementary Video 1

In situ deformation and recovery process of silicone rubber and poly(TA–CCO). Both silicone rubber and poly(TA–CCO) exhibit a high degree of elastic recovery after unloading. But at the same load, the silicone rubber was deformed nearly 40 times more than poly(TA–CCO), demonstrating the hard but elastic properties of poly(TA–CCO).

Source data

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Fang, W., Mu, Z., He, Y. et al. Organic–inorganic covalent–ionic molecules for elastic ceramic plastic. Nature 619, 293–299 (2023). https://doi.org/10.1038/s41586-023-06117-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/s41586-023-06117-1

This article is cited by

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing